A wide-angle X-ray study of the development of molecular orientation in crosslinked natural rubber

Mitchell, G.R. (1984) A wide-angle X-ray study of the development of molecular orientation in crosslinked natural rubber. Polymer, 25 (11). pp. 1562-1572. ISSN 0032-3861 doi: 10.1016/0032-3861(84)90148-4

Abstract/Summary

Molecular orientation parameters have been measured for the non-crystalline component of crosslinked natural rubber samples deformed in uniaxial tension as a function of the extension ratio and of temperature. The orientation parapeters 〈P2(cosα)〉 and 〈P4(cosα)〉 were obtained by an analysis of the anisotropy of the wide-angle X-ray scattering functions. For the measurements made at high temperatures the level of crystallinity detected was negligible and the orientation-strain behaviour could be compared directly with the predictions of molecular models of rubber elasticity. The molecular orientation behaviour with strain was found to be at variance with the estimates of the affine model particularly at low and moderate strains. Extension of the crosslinked rubber at room temperature led to strain-crystallization and measurements of both the molecular orientation of the non-crystalline chains and the degree of crystallinity during extension and relaxation enabled the role of the crystallites in the deformation process to be considered in detail. The intrinsic birefringence of the non-crystalline component was estimated, through the use of the 〈P2(cosα)〉 values obtained from X-ray scattering measurements, to be 0.20±0.02.

Item Type	Article
URI	https://reading-clone.eprints-hosting.org/id/eprint/26829
Item Type	Article
Refereed	Yes
Divisions	Interdisciplinary centres and themes > Chemical Analysis Facility (CAF) > Electron Microscopy Laboratory (CAF)
Publisher	Elsevier
Download/View statistics	View download statistics for this item